MIG Welding Stainless Steel

MIG Welding Stainless Steel

Although welding stainless steel may not be as difficult as welding aluminum, the metal does have its specific properties that vary from your more common steels.

When MIG welding on stainless, you usually have three choices of transfer depending on your equipment: spray-arc, short-circuiting, or pulsed-arc transfer.

......Read More......

Posted by Ardne at 12:29 PM 0 comments Links to this post

Labels: Gas Metal Arc Welding, GMAW, MIG Welding, Shielding Gas, Spray Transfer

Tuesday, February 27, 2007

Common Problems and Remedies for GMAW (Part 2)

Improper Bead Problem #2: TechniqueA concave or convex-shaped bead may also be caused by using an improper welding technique. For example, a push or forehand technique tends to create a flatter bead shape than a pull or backhand technique.RemedyFor best bead shapes, it is recommended to use a push angle of 5-10 degrees.

Improper Bead Problem #3: Inadequate Work CableProblems with the work cable can result in inadequate voltage available at the arc. Evidence of a work cable problem would be improper bead shape or a hot work cable.

RemedyWork cables have a tendency to overheat if they are too small or excessively worn. In replacing the cable, consult a chart to determine size based on length and current being used. The higher the current and longer the distance, the larger the cable needed.

III. Lack of FusionIf the consumable has improperly adhered to the base metal, a lack of fusion may occur. Improper fusion creates a weak, low quality weld and may ultimately lead to structural problems in the finished product.

Lack of Fusion Problem: Cold Lapping in the Short Arc Transfer ProcessIn short arc transfer, the wire directly touches the weld pool and a short circuit in the system causes the end of the wire to melt and detach a droplet. This shorting happens 40 to 200 times per second. Fusion problems may occur when the metal in the weld pool is melted, but there is not enough energy left to fuse it to the base plate. In these cases, the weld will have a good appearance, but none of the metal has actually been joined together. Since lack of fusion is difficult to detect visually, it must be checked by dye-penetrant, ultrasonic or bend testing.

Remedies:To guarantee correct fusion, ensure that voltage and amperage are set correctly. If the operator is still having problems after making those adjustments, it may require a change in the welding technique. For example, changing to a flux-cored wire or using the spray arc transfer method instead. In spray arc transfer, the arc never goes out so cold lapping and lack of fusion are not issues. Spray arc welding takes place at amperages high enough to melt the end of the wire and propel the droplet across the arc into the weld puddle.

IV. Faulty Wire DeliveryIf the wire is not feeding smoothly or if the operator is experiencing a chattering sound within the gun cable, there may be a problem with the wire delivery system. Most of the problems related to wire delivery are attributed to equipment set-up and maintenance.

Faulty Wire Delivery Problem #1: Contact Tip There is a tendency among operators to use oversized tips, which can lead to contact problems, inconsistencies in the arc, porosity and poor bead shape.

Remedies:First, make sure that the contact tip in the gun is in working order and sized appropriately to the wire being used. Visually inspect the tip and if it is wearing out (becoming egg-shaped), it will need to be replaced.

Faulty Wire Delivery Problem #2: Gun Liner A gun liner, like the contact tip, must be sized to the wire being fed through it. It also needs to be cleaned or replaced when wire is not being fed smoothly.

Remedy:To clean the liner, blow it out with low-pressure compressed air from the contact tip end, or replace the liner.

Faulty Wire Delivery Problem #3: Worn Out GunInside the gun are very fine strands of copper wire that will eventually break and wear out with time. Remedy:If the gun becomes extremely hot during use in one particular area, that is an indication that there is internal damage and it will need to be replaced. In addition, be certain that the gun is large enough for the application. Operators like to use small guns since they are easy on the hand, but if the gun is too small for the application, it will overheat.

Faulty Wire Delivery Problem #4: Drive Roll Drive rolls on the wire feeder periodically wear out and need to be replaced. Remedies:There are usually visual indications of wear on the grooves of the rolls if replacement is necessary. Also, make sure that the drive roll tension is set properly. To check tension, disconnect the welding input cable from the feeder or switch to the cold feed option. Feed the wire and pinch it as it exits the gun with the thumb and forefinger. If the wire can be stopped by pinching, more drive roll tension is needed.

The optimum tension will be indicated by feeding that is not stopped while pinching the wire. If the drive roll tension is too high, it may deform the wire leading to birdnesting (tangling) and a burn back (when the arc climbs the wire and fuses the wire to the contact tip.) Make sure that the drive rolls and the guide tube are as close together as possible. Next, check the path from where the wire leaves the reel to where it enters the drive rolls. The wire must line up with the incoming guide tubes so there is no scrapping of the wire as it goes through the tube. On some wire feeders, the wire spool position is adjustable -- align it so that it makes a straight path into the tube.

Faulty Wire Delivery Problem #5: Wire Coming Off Reel and TanglingSome wire feeding problems occur because the inertia from the wire reel causes it to coast after the gun trigger is released.Remedy:If the reel continues to coast, the wire on the reel will loosen and the wire may come off or become tangled. Most wire feeding systems have an adjustable brake on the wire reel. The brake tension should be set so that the reel does not coast. By following these four guidelines, a GMAW operator new to the world of welding or even someone more experienced should have an easier time diagnosing problems before they affect the quality of the work.

Source : Lincoln Electric Company

......Read More......

Posted by Ardne at 8:31 AM 0 comments Links to this post

Labels: Gas Metal Arc Welding

Common Problems and Remedies for GMAW (Part 1)

In much the same way that the automatic transmission has simplified the process of driving, Gas Metal Arc Welding (GMAW) has simplified the process of welding. Of all welding methods, GMAW is said to be one of the easiest to learn and perform. The main reason is because the power source does virtually all the work as it adjusts welding parameters to handle differing conditions; much like the sophisticated electronics of an automatic transmission.Because less skill is required, many operators are able to GMA weld at an acceptable level with limited training. These same operators run into trouble, however, when they begin creating inferior welds and are unable to diagnose and correct their own problems.

The guidelines listed below will help even inexperienced operators create high quality welds as well as offering tips for those who have been using the GMAW process for a number of years. Most common welding problems fall into four categories:

I. Weld porosity, II. Improper weld bead profile, III. Lack of fusion, and IV. Faulty wire delivery related to equipment set-up and maintenance.

I. Weld Metal PorosityPorosity

Problem #1: Improper Surface ConditionsThe most common cause of weld porosity is an improper surface condition of the metal. For example, oil, rust, paint or grease on the base metal may prevent proper weld penetration and hence lead to porosity. Welding processes that generate a slag such as Shielded Metal Arc Welding (SMAW) or Flux-Cored Arc Welding (FCAW) tend to tolerate surface contaminates better than GMAW since components found within the slag help to clean the metal’s surface. In GMAW, the only contamination protection is provided by the elements which are alloyed into the wire.

RemediesTo control porosity, use a deoxidizer within the wire such as silicon, manganese or trace amounts of aluminum, zirconium or titanium. Wire chemistry can be determined by referring to the American Welding Society (AWS) wire classification system. Test the various types of wire available to find the right chemistry for a given application. To start, try the most common wire type, ER70S-3 (Lincoln L50) which contains 0.9-1.4 percent manganese and 0.45-0.75 percent silicon. If porosity is still present in the finished weld, increase the amount of silicon and manganese found in the wire by switching to an ER70S-4 (Lincoln L54) or an ER70S-6 which has the highest levels of silicon (0.8 -1.15 percent) and manganese (1.4-1.8 percent). Some operators prefer to use a triple deoxidizer such as ER70S-2 (Lincoln L52) which contains aluminum, zirconium or titanium in addition to the silicon and manganese.In addition to changing the wire, further prevent porosity by cleaning the surface of the metal with a grinder or chemical solvents (such as a degreaser.) A word of caution though if using solvents, be certain not to use a chlorinated degreaser such as trichlorethylene near the welding arc -- the fume may react with the arc and produce toxic gases.

Porosity Problem #2: Gas Coverage The second leading cause of porosity in welds is a problem with the shielding gas coverage. The GMAW process relies on the shielding gas to physically protect the weld puddle from the air and to act as an arc stabilizer. If the shielding gas is disturbed, there is a potential that air could contaminate the weld puddle and lead to porosity.Remedies Shielding gas flow varies depending on wire size, amperage, transfer mode and wind speed. Typical gas flow should be approximately 30-40 cubic feet per hour. Using a flow meter, check that the shielding gas flow is set properly. There are a variety of flow meters on the market today ranging from simple dial gauges to ball flows all the way up to sophisticated, computerized models. Some operators mistakenly think that a pressure regulator is all that is needed, but the pressure meter will not set flow. A pure carbon dioxide shielding gas requires the use of special flow meters designed specifically for carbon dioxide. These special flow meters are not affected by the frosting that may occur as the carbon dioxide changes from liquid form to a gas.If high winds are blowing the shielding gas away from the puddle, it may be necessary to erect wind screens. According to the AWS Structural Welding Code, it is advisable not to GMA weld when wind speeds are greater than 5 mph. Indoors, ventilation systems may hamper gas coverage. In this case, redirect air flow away from the puddle. If fume extraction is necessary, use equipment designed specifically for this purpose such as MAGNUM™ Extraction Guns from Lincoln Electric -- they will remove the fume, but not disturb the shielding gas.A turbulent flow of gas as it exits the gun may also lead to porosity problems. Ideally, the gas will lay over the weld puddle much like a blanket. Turbulent gas flow can be caused by too high a flow, an excessive amount of spatter inside the gun nozzle, or spatter build-up in the gas diffuser. Other possible causes of insufficient gas flow may be damaged guns, cables, gas lines, hoses or loose gas fittings. These damaged accessories may create what is referred to as a “venturi effect” where air is sucked in through these openings and flow is reduced.Lastly, welding with a drag or backhand technique can lead to gas coverage problems. Try to weld with a push or forehand technique which lays the gas blanket out ahead of the arc and lets the gas settle into the joint. Porosity Problem#3: Base Metal PropertiesAnother cause of weld porosity may be attributed simply to the chemistry of the base metal. For instance, the base metal may be extremely high in sulfur content. Remedy Unfortunately, if the problem with porosity lies within the base metal properties, there is not much that can be done. The best solution is to use a different grade of steel or switch to a slag-generating welding process.II. Improper Weld Bead ProfileIf operators are experiencing a convex-shaped or concave-shaped bead, this may indicate a problem with heat input or technique. Improper Bead Problem #1: Insufficient Heat InputA convex or “ropy” bead indicates that the settings being used are too cold for the thickness of the material being welded. In other words, there is insufficient heat in the weld to enable it to penetrate into the base metal.

Remedies

To correct a problem with running “too cold,” an operator must first determine if the amperage is proper for the thickness of the material. Charts are available from the major manufacturers, including Lincoln Electric, that provide guidelines on amperage use under varying conditions. If the amperage is determined to be high enough, check the voltage. Voltage that is too low usually is accompanied by another telltale sign of a problem: a high amount of spatter. On the other hand, if voltage is too high, the operator will have problems controlling the process and the weld will have a tendency to undercut. One way to check if the voltage is set properly is to test it by listening. A properly running arc will have a certain sound. For instance, in short arc transfer at low amperages, an arc should have a steady buzz. At high amperages using spray arc transfer, the arc will make a crackling sound. The arc sound can also indicate problems -- a steady hiss will indicate that voltage is too high and the operator is prone to undercut; while a loud, raspy sound may indicate voltage that is too low. (continued)

(Source : Lincoln Electric Company)

......Read More......

Posted by Ardne at 8:19 AM 0 comments Links to this post

Labels: Gas Metal Arc Welding

Monday, February 26, 2007

GMAW Metal Transfer Mode

Spray transfer GMAW was the first metal transfer method used in GMAW, best suited for welding aluminum and stainless steel while employing an inert shielding gas and a relatively thick electrode.

Molten metal droplets (with diameters smaller than the electrode diameter) are rapidly passed along the stable electric arc from the electrode to the workpiece, essentially eliminating spatter and resulting in a high-quality weld finish.

High amounts of voltage and current are necessary, which means that the process involves high heat input and a large weld area and heat-affected zone.

Short-circuiting

Further developments in welding steel with GMAW led to a variation known as short-circuiting or short-arc GMAW, in which carbon dioxide shields the weld, the electrode wire is smaller, and the current is lower than for the globular method.

As a result of the lower current, the heat input for the short-arc variation is reduced, making it possible to weld thinner materials while decreasing the amount of distortion and residual stress in the weld area.

Pulsed-spray

The pulse-spray metal transfer mode is based on the principles of spray transfer but uses a pulsing current to melt the filler wire and allow one small molten droplet to fall with each pulse.

The pulses allow the average current to be lower, decreasing the overall heat input and thereby decreasing the size of the weld pool and heat-affected zone while making it possible to weld thin work pieces.

The pulse provides a stable arc and no spatter, since no short-circuiting takes place. This also makes the process suitable for nearly all metals, and thicker electrode wire can be used as well.

The smaller weld pool gives the variation greater versatility, making it possible to weld in all positions.

It generates lower heat input and can be used to weld thin work pieces, as well as nonferrous materials.

Globular

GMAW with globular metal transfer is often considered the most undesirable of the four major GMAW variations, because of its tendency to produce high heat, a poor weld surface, and spatter.

The method was originally developed as a cost efficient way to weld steel using GMAW, because this variation uses carbon dioxide, a less expensive shielding gas than argon.

wikipedia.com

......Read More......

Posted by Ardne at 12:39 PM 0 comments Links to this post

Labels: Gas Metal Arc Welding

Newer Posts

Older Posts

Home

Subscribe to: Posts (Atom)

MORE ARTICLELive Search News: WELDING

Updated :

Van fire sparks major incident

Thurrock Gazette - ... brought a large part of north Essex to a standstill today when the A12 and the railway line to London were closed because of a van that caught fire. The Ford Transit, which belongs to Essex Fire and Rescue Service, was carrying a portable welding ...

Publ.Date : Fri, 05 Oct 2007 18:31:00 GMT

Wolffe: Terry McAuliffe's Mission

MSNBC - Oct. 5, 2007 - The scene did not exactly reek of triumph. Just two dozen supporters had gathered at the union hall perched between a welding company and a gas station in Cedar Rapids, Iowa. The room was two-thirds empty, the sign-up sheets on the ...

Publ.Date : Fri, 05 Oct 2007 16:51:00 GMT

Rockies Express Pipeline makes its way to Randolph County

Moberly Monitor-Index & Democrat - Besides the crew members, Spread 7 consists of a chief inspector, who oversees the entire project; two to three assistant inspectors, who are constantly overseeing the work; 10 welding inspectors, an environmental group of six, a safety group and a ...

Publ.Date : Fri, 05 Oct 2007 17:27:00 GMT

RSS Feed Reader

Increased Website Traffic